Hand Lay-up Fiberglass Resin Corrosion Resistant Acid and Alkali Resistant No Antimony Added Low Styrene Content Vinyl Resin Epoxy Vinyl Resin

• Customization: Available
• Molecular Principal Chain: Element Organic Polymer
• Color: Yellow
• Model NO.: 510
• ASTM E-84 Flame Spread: Class 2 (Less Than 76) Class 1 (with The Use of an
• Specifications: Brominated Fire-Retardant Epoxy Vinyl Ester Resin
• Dynamic Viscosity: 420mpas
• Kinematic Viscosity: 350cst
• Styrene Content: 37%
• Density: 1.138g/Ml
• Transport Package: IBC Tank/Drum
• Specification: 5.72cm * 5.72cm * 86.00cm
• Trademark: RealLand
• Origin: Changzhou China
• HS Code: 3905910000
• Production Capacity: 50000 Ton/Year

Product Description

 REL 510 Epoxy Vinyl Ester Resin

 

Product Description

 

REL 510 is a brominated epoxy vinyl ester resin that offers a high degree of fire retardance while providing excellent chemical resistance and toughness. Optimum fire retardance is achieved when antimony compounds are added to the resin. Laminates made with REL 510 resin have met ASTM E-84 Flame Spread "Class 2" rating (less than 75). With the use of antimony synergists,"Class 1" ratings can be achieved.


 

Our resins are a new generation of resins that can be used to improve fabrication efficiency and product quality. Their lighter color makes defects easier to see and correct while the resin is still workable. The resin's improved reactivity properties often permit an increase in lay-up thickness wet on wet. The superior stability also provides additional storage and handling flexibility for the fabricator. REL 510  resin contains only 37 weight % styrene, resulting in reduced styrene emissions.

 

 

Equipment fabricated with REL 510 resin offer excellent corrosion resistance to a wide range of acids, alkalis, bleaches and organic compounds and retains its strength, heat and chemical resistant properties when exposed to hot gases and flamable liquids.

 

 

 

Detailed Photos

 

 

Features & Applications

REL 510 resin is designed for ease of fabrication using hand lay-up, spray-up, flament winding, compression molding, resin transfer molding and pultrusion techniques. This resin is used extensively in FRP duct work, stacks and stack-liner applications. it is also suitable for equipment handling mixtures of air and hot gases, building panels and flooring compounds where a degree of ignition inhibiting properties are needed.

 

REL 510 resin resists mechanical and chemical damage enabling use in various caustic environments such as sodium hypochlorite, chlorine dioxide and alkaline hydrogen peroxide.

Recommendations for specific services and environments can be provided by contacting us.

 

Product Parameters

 

Typical geltimes(2) using NOROX(3) MEKP-925H(4) catalyst (MEKP) and Cobalt Naphthenate or Octoate-6%(5)(Cobalt6%), Diethylaniline(7)(DEA) and 2,4-Pentanedione (2,4-P)
 

Geltime at 15'C(59°F)	MEKP(phr)	Cobalt6%(phr)	DEA(phr)
15 +/-5 minutes	1.50	0.30	1.25
30 +/-5 minutes	1.50	0.12	-
60 +/- 5 minutes	1.25	0.05	-

 

Geltime at 20'C(68°F)	MEKP(phr)	Cobalt6%(phr)	2,4-P(phr)
15 +/- 5 minutes	1.25	0.20	-
30 +/- 5 minutes	1.25	0.05	-
60 +/-5 minutes	1.25	0.10	0.03

 

Geltime at 25°C(77°F)	MEKP(phr)	Cobalt6%(phr)	2,4-P(phr)
15 +/- 5 minutes	1.00	0.10	-
30 +/- 5minutes	1.00	0.05	0.01
60 +/-5minutes	1.00	0.05	0.025

 

Geltime at 30°C (86°F)	MEKP(phr)	Cobalt6%(phr)	2,4-P(phr)
15 +/- 5 minutes	1.00	0.05	-
30 +/- 5minutes	1.00	0.05	0.02
60 +/-5 minutes	1.00	0.05	0.04

 

Geltime at 35°C (95°F)	MEKP(phr)	Cobalt6%(phr)	2,4-P(phr)
15 +/- 5 minutes	1.00	0.05	0.02
30 +/- 5minutes	1.00	0.05	0.04
60 +/-5 minutes	1.00	0.05	0.07

(2) Thoroughly test any other materials in your applications before full-scale use. Geltimes may vary dueto the reactive nature of these materials. Always test a small quantity before formulating large quantities
(3)Registered trademark of Norac Inc.
(4) NOrOx MEKP-925H content MEKP. Use of other MEKP catalystsor additives may result in different gel times.
(5) Use of cobalt octoate, especially in combination with 2.4-P can result in 20-30% slower gel times
(6)phr= parts per hundred resin molding compound

 

Performance

Casting Properties

Property(2) or clear casting(7) at 25°C(77°F)	Value (sl)	Method	Value (US)	Method
Tensile strength	86 MPa	ISO 527	12000 psi	ASTM D638
Tensile modulus	3200 MPa	ISO 527	460 kpsi	ASTM D638
Elongation, Yield	5-6%	ISO 527	5-6%	ASTM D638
Flexural strength	150 MPa	ISO 178	22000 psi	ASTM D790
Flexural modulus	3400 MPa	ISO 178	490 kpsi	ASTM D790
Heat distortion temperature	105ºC	ISO 75	220°F	ASTM D648
Glass transition temperature,Tg2	120°C	ISO 11359	250°F	ASTMD3419
Volume shrinkage	7.8 %	-	7.8 %	-
Barcol Hardness	35	EN 59	35	ASTMD2583

(7)The properties in the table are measured from a clear resin casting which is postcured for 24h at room temperature and 2 hours at 120ºC/ 250°F. (The Sl values are reported to two significant figures and US standard values based on conversion.)


Laminate Properties
 

Property(2)of6mm(¼ in.) laminate(8) at 25°C(77°F)	Value (sl)	Method	Value (US)	Method
Tensile strength	150 MPa	ISO 527	22000 psi	ASTM D3039
Tensile modulus	12000 MPa	ISO 527	1700 kpsi	ASTM D3039
Flexural strength	210 MPa	ISO 178	30000 psi	ASTM D790
Flexural modulus	8100 MPa	ISO 178	1200 kpsi	ASTM D790
Glass content	40%	ISO 1172	40%	ASTM D2584

(8)Laminate postcured 24 hours at room temperature and 6 hours at 80 ºC (175 F). Laminate construction isV/W/M/Wr/M/Wr/M where V=Continuous veil glass, M=Chopped strand mat 450 g/m2 (1.5 oz/ft2) and Wr=Wowen roving 800 g/m2 (24 oz/vd2).(The Sl values are reported to two significant figures and US standard values are based on conversion).

 

Company Profile

 

Certifications

 

 

FAQ

Q: Can I Request a Sample of Unsaturated Polyester Resin?
A: Yes,we can provide 10kg of resin as a free sample, but freight are typically the responsibility of the buyer. 

Q: Can I Customize the Formulation of Unsaturated Polyester Resin for My Project?
A: Yes, absolutely. We understand that different projects may have unique requirements. Our R & D department is well-equipped to handle custom formulations based on your specific needs. You can provide us with the details of your project, including any specific characteristics or performance criteria you are looking for, and our experts will work on tailoring a formulation that meets your requirements.

Q: How Do I Choose the Right Unsaturated Polyester Resin for My Application?
A: We would provide guidance on selecting the appropriate UPR based on different project requirements.
 
Q: What Certifications and Quality Standards Does Your Unsaturated Polyester Resin Meet?
A: Our Unsaturated Polyester Resin meets CCS, RoHS, REACH, EMS, and QMS certifications and quality standards.

Q: What is The Product Lead Time?
A: 10 days.
 
Q:What's Shelf Life of Unsaturated Polyester Resin ?
A: Normally 8 months.

Q:Can I Get a Lower Price for a Large Quantity Order ?
A: Absolutely. The online price serves as a reference, but due to fluctuations in raw material costs, our sales team can provide you with the most accurate and competitive pricing. Before making a purchase, kindly engage with our sales representatives. They will work closely with you, taking into account your order quantity and specific requirements, to ensure you receive the best and most cost-effective pricing tailored to your needs.