| Molecular Principal Chain: | Element Organic Polymer |
|---|---|
| Color: | Yellow |
| Specifications: | Bisphenol a Epoxy Vinyl Ester |
| Acid Value: | 5.0-13.0 Mg KOH/ G Sample |
| Geltime(25ºC): | 10-30min |
| Customized: | Available |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier BST-U400 is a modified one-component polyurethane resin. This product completes the polymerization reaction of two-component polyurethane (isocyanate and polyol) during the production process, and the user uses a free radical polymerization curing method similar to unsaturated polyester resin and vinyl ester resin; while retaining the performance of two-component polyurethane resin, it also has the characteristics of good processability, good adaptability to the production environment, and low equipment requirements.
The composite material manufactured with this product has excellent toughness and interface bonding strength, can give full play to the fiber performance, and obtain high-performance composite material products. The polyurethane segment content in the BST-U400 cured product is about 50%, which is mainly suitable for pultrusion molding process.
| BST-U400 | |
| Appearance | Brown liquid |
| Viscosity (mPa.s ,25ºC) | 300-600 |
| density (g/cm3 ,25ºC) | 1.0- 1.1 |
| Solid content(%) | 55-65 |
| storage temperature(ºC) | Normal temperature |
| Test items | Values | Unit | Test method |
| Tensile strength | 77 | MPa | ISO 527-2 |
| Tensile modulus | 3 | GPa | ISO 527-2 |
| Tensile elongation | 6.7 | % | ISO 527-2 |
| Flexural strength | 118 | MPa | GB/T 2570- 1995 |
| Flexural modulus | 3.2 | GPa | GB/T 2570- 1995 |
| Impact toughness | 37 | (KJ/m2) | GB 2571-81 |
| Glass transition temperature | 96 | ºC | DSC |
| Test items | Values | Unit | Test method |
| Tensile strength | 445 | MPa | GB/T 1447-2005 |
| Tensile modulus | 25 | GPa | GB/T 1447-2005 |
| Tensile elongation | 2.6 | % | GB/T 1447-2005 |
| Flexural strength | 610 | MPa | GB/T 1449-2005 |
| Flexural modulus | 25.6 | GPa | GB/T 1449-2005 |
| Test items | Values | Unit | Test method |
| Longitudinal tensile strength | 728 | MPa | GB/T 1447-2005 |
| Longitudinal tensile modulus | 53.5 | GPa | GB/T 1447-2005 |
| Transverse tensile strength | 39.1 | MPa | GB/T 1447-2005 |
| Transverse tensile modulus | 17 | GPa | GB/T 1447-2005 |
| Longitudinal bending strength | 1040 | MPa | GB/T 1449-2005 |
| Longitudinal flexural modulus | 42.9 | GPa | GB/T 1449-2005 |
| Transverse bending strength | 125 | MPa | GB/T 1449-2005 |
| Transverse bending modulus | 16.3 | GPa | GB/T 1449-2005 |
Q: Can I Request a Sample of Unsaturated Polyester Resin?
A: Yes,we can provide 10kg of resin as a free sample, but freight are typically the responsibility of the buyer.
Q: Do you have OEM/ODM service?
A: Yes, we are highly flexible in offering OEM/ODM services.
Q: What Certifications and Quality Standards Does Your Unsaturated Polyester Resin Meet?
A: Our Unsaturated Polyester Resin meets CCS, RoHS, REACH, EMS, and QMS certifications and quality standards.
Q: What is The Product Lead Time?
A: 10 days.
Q:What's Shelf Life of Unsaturated Polyester Resin ?
A: Normally 8months.
Q: Can I Customize the Formulation of Unsaturated Polyester Resin for My Project?
A: Yes, absolutely. We understand that different projects may have unique requirements. Our R & D department is well-equipped to handle custom formulations based on your specific needs. You can provide us with the details of your project, including any specific characteristics or performance criteria you are looking for, and our experts will work on tailoring a formulation that meets your requirements.
Q: How Do I Choose the Right Unsaturated Polyester Resin for My Application?
A: We would provide guidance on selecting the appropriate UPR based on different project requirements.